Method of flux-free soldering of aluminum-containing workpieces in a controlled atmosphere

ABSTRACT

A furnace for flux-free soldering of aluminum-containing workpieces in a controlled atmosphere has a furnace chamber through which workpieces to be soldered are made to travel. The furnace chamber itself is a gas-tight metallic muffle which is thermally insulated from the outer part of the furnace and has an inlet for the workpieces and an outlet for them. A first lock chamber is interposed between the furnace chamber and the inlet, and a second lock chamber is interposed between the outlet and the furnace chamber. Arrangements are provided for admitting vacuum and protective gas into the lock chambers, and protective gas into the muffle and a heating arrangement is provided for heating the controlled atmosphere in the muffle.

United States Patent [191 Kendziora et al.

[451 May 13, 1975 METHOD OF FLUX-FREE SOLDERING OF ALUMINUM-CONTAINING WORKPIECES IN A CONTROLLED ATMOSPHERE [75] Inventors: Keinz Kendziora, Bonn; Johannes Nenner, Bornheim-Merteh; Heinz Schoer, Alfter; Werner Schultze, Bonn, all of Germany [30] Foreign Application Priority Data Nov. 9, 1972 Germany 2254769 [52] US. Cl. 228/200; 228/219; 228/222; 228/232 [51] Int. Cl B23k 31/02 [58] Field of Search 29/429, 430, 470, 484, 29/488, 494, 498; 432/128 [56] References Cited UNITED STATES PATENTS Kugel 432/128 Primary ExaminerAl Lawrence Smith Assistant ExaminerMargaret M. Joyce Attorney, Agent, or Firm-Michael S. Striker [5 7] ABSTRACT A furnace for flux-free soldering of aluminumcontaining workpieces in a controlled atmosphere has a furnace chamber through which workpieces to be soldered are made to travel. The furnace chamber itself is a gas-tight metallic muffle which is thermally insulated from the outer part of the furnace and has an inlet for the workpieces and an outlet for them. A first lock chamber is interposed between the furnace chamber and the inlet, and a second lock chamber is interposed between the outlet and the furnace chamber. Arrangements are provided for admitting vacuum and protective gas into the lock chambers, and protective gas into the muffle and a heating arrangement is provided for heating the controlled atmosphere in the muffle.

9 Claims, 3 Drawing Figures PATENI MAY 1 ams SHEET 2 0F 2 METHOD OF FLUX-FREE SOLDERING OF ALUMINUM-CONTAINING WORKPIECES IN A CONTROLLED ATMOSPHERE This is a division, of application Ser. No. 411,383, filed Oct. 31, 1973.

BACKGROUND OF THE INVENTION The present invention relates generally to the soldering of aluminum-containing workpieces, and more particularly to the flux-free soldering of such workpieces in a controlled atmosphere. In particular, the invention relates to a furnace for flux-free soldering of aluminumcontaining workpieces in a controlled atmosphere, and a method of carrying out such soldering.

The conventional way of soldering aluminum work pieces and those which contain aluminum is to use flux of one of the well known types. It is known from the prior art to effect flux soldering of aluminumcontaining workpieces in furnaces which are constructed as air-circulating furnaces. These furnaces must be largely constructed of ceramic materials because other materials are strongly attacked by the flux substances. Another approach from the prior art is to solder in metallic furnaces which do not require the use of ceramic materials, and wherein the soldering is carried out in a hard vacuum. However, this type of furnace cannot be used for soldering without flux and under a protective gas atmosphere. The reason is that in this latter type of furnace, which must be heated by radiation, the outer wall is constructed as a watercooled double wall against which heat radiation is directed. This principal cannot be used in furnaces using a protective gas atmosphere because otherwise the heated protective gas would predominantly yield to the watercooled wall of the furnace rather than to the workpieces.

SUMMARY OF THE INVENTION It is a general object of the present invention to overcome the disadvantages of the prior art, and to permit flux-free soldering of aluminum-containing workpieces in a controlled atmosphere.

More particularly, it is an object of the present invention to provide an improved furnace for flux-free soldering of aluminum-containing workpieces in a controlled atmosphere.

Another object of the invention is to provide a method of carrying out such flux-free soldering of aluminum-containing workpieces in a controlled atmosphere.

In keeping with the above objects, and with others which will become apparent hereafter, one feature of the invention resides in a furnace for flux-free soldering of aluminum-containing workpieces in a controlled atmosphere. Briefly stated, this comprises a combination of wall means defining a furnace chamber through which workpieces to be soldered are to travel. The furnace chamber is a gas-tight metallic muffle, being thermally insulated from the outer part of the furnace and being adapted to contain such workpieces in a controlled atmosphere. The muffle has an inlet for the entry of the workpieces and an outlet for the exit of the treated or soldered workpieces. A first lock chamber is interposed between the furnace chamber and the inlet, and second lock chamber is interposed between the furnace chamber and the outlet. Admitting means is provided for admitting vacuum and protective gas into the lock chambers and protective gas into the muffle and heating means is provided for heating the controlled atmosphere in the muffle.

The novel features which are considered as characteristic for the invention are set forth in particular in the appended claims. The invention itself, however, both as to its construction and its method of operation, together with additional objects and advantages thereof will be best understood from the following description of specific embodiments when read in connection with the accompanying drawing.

BRIEF DESCRIPTION OF THE DRAWING FIG. 1 is a somewhat diagrammatic vertical longitudinal section through a furnace according to the present invention;

FIG. 2 is a section taken on line AA of FIG. 1; and

FIG. 3 is a section taken on line BB of FIG. 1.

DESCRIPTION OF THE PREFERRED EMBODIMENTS Referring firstly to FIG. 1, it will be seen that the workpieces to be soldered, which are aluminum workpieces or aluminum-containing workpieces and are not specifically illustrated, are supplied via a charging table 1 provided with rollers 2 on which the workpieces are rolled until they enter a preheating chamber 3. Located in the preheating chamber 3 is a blower 4 which is driven by a motor 40 (see FIG. 3) and which serves to provide for uniform circulation of air in the chamber 3. This air has been heated by electrical heating elements 5 which are also most clearly shown in FIG. 3.

The workpieces to be soldered pass from the rollers 2 onto a conveyor 6 which advances them (towards the right in FIG. 1) into a lock chamber 7. The lock chamber 7 has gates 8 and 9 which can be raised and lowered via motors 10 and 11 and ropes or similar elements 12, 13 which are connected with the motors 10 and 11 and with the respective gates. A set of roller 14 is arranged in the lock chamber 7 to permit advancement of the workpieces to travel through the lock chamber 7 and into a gas-tight metallic muffle 15. The muffle may advantageously be made of steel and is in itself known from muffle furnaces which have long been used in the steel producting industry. At the other end of the muffie 15 there is arranged a further lock chamber 17 through which the soldered workpieces are discharged into a cooling chamber 18. To accommodate movements of the muffle 15 and of the metallic lock chamber 17 which result from thermal expansion or contraction of their material, and muffle 15 and the lock chamber 17 are mounted on rollers 16.

When the workpieces enter the muffle 15 they move onto conveyors l9 and 20 on which they travel through the muffle towards the lock chamber 17. On the conveyor 19 the workpieces are preheated until they are just below the soldering temperature, and the actual soldering operation takes place when the workpieces then move onto the conveyor 20.

Reference numerals 21 designate blowers which are operated by motors 21a (only one shown), and details of this arrangement are also visible in FIG. 2. That Figure also shows that heating elements 22 extend gastightly into the muffle 15 in order to permit heating of the protective-gas atmosphere which exists in the muffle 15 and which is constantly being circulated within the same by the blowers 21. The protective gas is introduced intothe muffle by pipes 38 and the pressure in the muffle is controlled by a valve 39. A temperature measuring rail 23 is provided for determining the temperature of the workpieces to be soldered, and for controlling the speed of movement of the conveyor 19 in response to the measured temperature. A further similar device 24 controls in the same. manner the actual soldering operation which takes place on the conveyor Gates 25 and 32 are provided, of which the former connects the outlet end of the muffle with the lock.

chamber 17, whereas the gate 32 connects the interior of the lock chamber 17 with the furnace chamber in general, and in particular with the cooling zone or chamber 18. The gates and 32 can be raised and lowered via ropes or the like 26 and 32a which are operated by motors 27 and 33, respectively.

The lock chamber 7 is provided with an inlet 28 and the lock chamber 17 with an inlet 28', and in both cases these serve to evacuate the lock chambers. Conduits 29 and 29' are provided, which can be opened or closed by means of valves 3(1), 30 and which permit the introduction of protective gas into the lock chambers 7, 17.

When the soldered workpieces enter the lock chamber 17, they are transported through the same on rollers 31 and, when the gate 32 has been raised via the motor 33, they can then enter into the chamber 18. it will be appreciated that the gate 32 is raised only when the gate 25 is in lowered closed position, which is, of course, also true with respect to the gates 8 and 9 of the lock chamber 7.

During passage through the zone or chamber 18, the soldered workpieces travel on a conveyor 34 and are permitted to cool down. If it is desired to provide a sudden cooling of shock-like nature, for instance by directing an air blast against the workpieces, then blowers 35 may be turned on which are provided for this purpose in the zone 18. Finally, the workpieces move onto the rollers 36 and are conveyed away to be removed. The passage of the workpieces through the entire furnace may be controlled in various ways, for instance by means of the light-beam sensors 37 which are shown only diagrammatically.

A particular advantage of the furnace according to the present invention is the fact that no ceramic materials whatsoever are required for the interior of the furnace. This advantage results from the fact that ceramic materials have considerable capability of absorbing oxygen and moisture, which brings with it the danger that the protective atmosphere of the furnace, and in particular the muffle 15, might be contaminated. Insofar as any insulating material is used in the furnace according to the present invention, there is no connection whatsoever between such material and the interior of the muffle 15. This is important because it excludes the possibility that any gaseous contaminants adhereing to or in some fashion resulting from such insulating material, might enter into the muffle 15 and contaminate the protective atmosphere therein. All ceramic materials, as well as asbestos and mineral wool are to be completely avoided in the interior of the muffle 15, be it as structural components, as packings, as sealing elements or the like.

Moreover, it has been found that grease, oil and vapor products thereof, as well as particles which are worn off rubber or synthetic plastic, such as off sealing elements ofsuch materials, also disadvantageously influence the soldering process if the soldering is carried out without flux. For this reason it is particularly advantageous if all seals which arerequired where shaftsgor the like for blowers, transporting roll ers or the like pass if through the wall of the furnace or of the muffle 15 into the interior of the latter, are metallictseals to the extent t possible. No additional lubrication is to be used, and no sealing elements of rubber, synthetic plastic or thelike are to be employed. Rather, the gapwhic h will inevitably exist between the respective shafts or the like and the metal of the wall of the muffle T5, is to be sealed by blowing a protective gas into. it. Alternatelyythe a walls of the muffle l5 need notbe perforate at alLand instead drive shafts or the like can have a first portion; 7 located outside the wall and a second portion located inwardlyof the wall Within the interior of themuffle 15,

vantageous if they are encapsulated 4 1, that is if they are completely covered at the interior of the: muffle. I

Seals which may for instance be required between the lock chambers 7, 17 and the furnace chamber or the I outer ambient atmosphere, can advantageously be made of silicone rubber if they are properlycooled. If stationary components are to be sealed, as opposedto components which move, then the seal is advantageously of a metallic nature.

Conduits or hoses whichsupply the protective danger that the protective gas itself would become connected with one another must, of course, be gas-tightly ing.

aluminum-containing workpieces without any interference and difficulties. Itis possible to establish in the novel furnace a protective gas atmosphere with an oxy-- 1 gen content which is low enough, and with a dew point which is low .enough,land to maintain these features. v

i This permits an increase in the thickness of the oxide layer, or an oxidation of the solder at its point of con-. nection with the workpieces, from being. prevented during the soldering operation. For economic reasons;

it is advantageous to use as the protective gas a; liquid purified nitrogen, which is commercially available and in itscommercial form already contains less than 5, ppm v 0 and has a dew point of lower than C. Of course,

absorbedair and moisture into: the furnace, and particularly into the muffle, because this would undesirably I 1 contaminate the protective atmosphere. To'avoid this.

gas i I must not .be of rubber or synthetic plastic material, such as for instance polyvinyl chloride. Such materials I are not suitable because their use would involve the connected, preferably by means of solderingor 'weld-Q The furnace according to the presentinvention makes possible a flux-less soldering of aluminum or and i we have found it to be advantageous to make the lock chamber 7, through which the workpieces enter into the muffle l5, heatable so that the workpieces can be preheated to at least 100C in the lock chamber 7 before they enter the muffle l5.

Quite surprisingly it has been found that independently of the thus far discussed furnace construction it is without disadvantage for the soldering without flux, if the workpieces to be soldered are preheated prior to entry into the lock chamber 7 in an air furnace, for instance an electrically heated air furnace, to a temperature up to a maximum of 500C. If this is done, heating of the lock chamber 7 itself is not absolutely necessary. Moreover, the dwell time required for the workpieces in the protective gas atmosphere of the muffle 15, and thereby the axial length of the muffle 15, can be reduced if the workpieces are so preheated.

The heating of the protective gas itself can be carried out in suitable manner, advantageously electrically. Of course, other types of heaters can also be used, for instance gas heating. It is also advantageous if the heated protective gas is circulated and kept in motion by blowers, to obtain a uniform temperature in the interior of the muffle 15, and to provide for a better and more uniform heating of the workpieces, particularly of larger workpieces.

The workpieces themselves can be directly measured as to their temperature, for instance by means ofa measuring device such as is disclosed in German Pat. application P 22 O6,72l.6 This type of device has been described in connection with FIGS. 13 and serves for thermal electric measurement of the temperature of one or more workpieces traveling through a furnace. It involves the mounting of a desired number of thermal elements in form of wires, rods or rails which are located in the particular zone of the furnace wherein the temperature of the workpiece or workpieces is to be measured and which extend in the direction of the moving workpiece. These thermal elements are insulated with respect to the muffle as well as with reference to one another, and either the positive or the neg ative arm is provided only once, whereas the arm with the other potential is provided as many times as temperature-measuring locations are desired. One end of the material of the thermal elements extends out of the muffle, being insulated to prevent entry or escape of atmosphere, and is connected with devices which readout the measured information. Such devices may be in the form of a temperature measuring or registering arrangement.

This manner of measuring the temperature of the workpieces in the sealed muffle 15 is particularly advantageous because it permits the quantity of discards (i.e., workpieces which have not been properly soldered due to being at improper temperatures) to be maintained very small. This is especially true if successive ones of the workpieces differ in size and/or configuration. Moreover, this type of arrangement can be used for controlling the speed at which the workpieces pass through the muffle, for instance in that the temperature which is obtained at the end of the preheating zone is measured and is used--if the actual temperature differs from a preselected reference value--to increase or decrease the speed at which the workpieces move through the muffle 15, or even to temporarily stop such movement. In fact, this control principal makes it possible to very precisely coordinate the length of the furnace, and in particular of the muffle 15, with the number and configuration of the workpieces to be soldered. Especially if small numbers of workpieces are involved, a very short muffle 15 with only a single temperature zone may be utilized, in which case the preheated workpieces are soldered in the protective atmosphere of the muffle while being stationary, rather than while traveling. Of course, preheating, entry of the materials through the lock 7 and exit of the soldered workpieces through the lock 17, would be the same as previously described.

If hardenable alloys are used as core workpieces, it is advantageous to rapidly cool the workpieces quite quickly after the soldering has taken place. To prevent distortions in the shape of the workpieces due to excessively rapid cooling, cooling with water should be foregone, and cooling with gas should be employed if the cooling is carried out while the workpieces are still in the protective atmosphere, for instance of the lock chamber 17. It is, however, economically more advantageous if the cooling is carried out only after they have left the lock chamber 17, because then it is possible to use simply air for cooling purposes. If cooling is carried out within the lock chamber 17, then it is necessary to use a cooled protective gas, for instance nitrogen, because otherwise excessive contamination of the protective atmosphehre by moisture or by oil vapors might take place if compressed air were used, and this would require prolonged withdrawal of the atmosphere from the chamber 17 and subsequent cleaning of the chamber before operations could be continued. Instead of containing a protective gas, the chamber 7 could be evacuated prior to opening of gate 9.

It will be understood that each of the elements described above, or two or more together, may also find a useful application in other types of constructions differing from the type described above.

While the invention has been illustrated and described as embodied in the flux-free soldering of aluminum-containing workpieces in a controlled atmosphere, it is not intended to be limited to the details shown, since various modifications and structural changes may be made without departing in any way from the spirit of the present invention.

Without further analysis, the foregoing will so fully reveal the gist of the present invention that others can by applying current knowledge readily adapt it for various applications without omitting features that, from the standpoint of prior art, fairly constitute essential characteristics of the generic or specific aspects of this invention and, therefore, such adaptations should and are intended to be comprehended within the meaning and range of equivalence of the following claims.

What is claimed as new and desired to be protected by Letters Patent is set forth in the appended claims.

1. In a method of flux-free soldering of aluminumcontaining workpieces in a controlled atmosphere, the steps of admitting the workpieces to be soldered into a preheating chamber; preheating said workpieces to at most 500C in said preheating chamber; admitting the thus preheated workpieces into a lock chamber containing a protective gas; admitting said workpieces from said lock chamber into a gas-tight muffle containing a controlled atmosphere, and effecting soldering in said controlled atmosphere; and discharging the soldered workpiece from said muffle through an additional lock chamber containing a protective gas, into a cooling Zone or chamber.

2. In a method according to claim 1, wherein said workpieces are heated in said gas-tight muffle to the soldering temperature.

3. In a method according to claim I, wherein said controlled atmosphere is a protective gas atmosphere 4. In a method according to claim 3, wherein said protective gas atmosphere in said muffle has a low oxygen content.

5. In a method according to claim 4, wherein said protective gas atmosphere having a low oxygen content is heated to the soldering temperature and circulated within said muffle. t

6. In a method according to claiml l, wherein the i soldered workpiece is cooled in: said coolingzonesor L chamber by directing an air. blast against said soldered.

workpiece.

7. In a method according to claim 1 whereinsaid 'controlled atmosphere consists of nitrogen.

8. In a method according to claim 7 wherein said nitrogen has a dew point of lower than -60 C-. 

1. In a method of flux-free soldering of aluminum-containing workpieces in a controlled atmosphere, the steps of admitting the workpieces to be soldered into a preheating chamber; preheating said workpieces to at most 500*C in said preheating chamber; admitting the thus preheated workpieces into a lock chamber containing a protective gas; admitting said workpieces from said lock chamber into a gas-tight muffle containing a controlled atmosphere, and effecting soldering in said controlled atmosphere; and discharging the soldered workpiece from said muffle through an additional lock chamber containing a protective gas, into a cooling zone or chamber.
 2. In a method according to claim 1, wherein said workpieces are heated in said gas-tight muffle to the soldering temperature.
 3. In a method according to claim 1, wherein said controlled atmosphere is a protective gas atmosphere.
 4. In a method according to claim 3, wherein said protective gas atmosphere in said muffle has a low oxygen content.
 5. In a method according to claim 4, wherein said protective gas atmosphere having a low oxygen content is heated to the soldering temperature and circulated within said muffle.
 6. In a method according to claim 1, wherein the soldered workpiece is cooled in said cooling zone or chamber by directing an air blast against said soldered workpiece.
 7. In a method according to claim 1 wherein said controlled atmosphere consists of nitrogen.
 8. In a method according to claim 7 wherein said nitrogen has a dew point of lower than -60* C.
 9. In a method according to claim 1 wherein the workpieces are preheated in said lock chamber to at least 100* C. 